| 产地/厂家：沙伯基础(原GE) | 类型：标准料 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 10.5 | g/10min | |
| 物理性能 | 模具收缩率 | 3.2mm | ASTM D-955 | 5-7 | 10-3 |
| 比重 | ASTM D-792 | 1.2 | |||
| 吸水率 | % | ASTM D-570 | 0.15 | ||
| 机械性能 | 拉伸强度 | 断裂点 | ASTM D-638 | 69 | MPa |
| 洛氏硬度 | R | ASTM D-785 | 118 | ||
| 弯曲模量 | ASTM D-790 | 2343 | MPa | ||
| 拉伸强度 | 屈伏点 | ASTM D-638 | 62 | MPa | |
| 拉伸率 | 断裂点 | ASTM D-638 | 130 | % | |
| 冲击强度 | 缺口23°C | ASTM D-256 | 800 | J/M | |
| 弯曲强度 | ASTM D-790 | 96 | MPa | ||
| 电气性能 | 损耗因数 | 60Hz | ASTM D-150 | 0.0009 | |
| 介电常数 | 60Hz | ASTM D-150 | 3.17 | ||
| 损耗因数 | 1MHz | ASTM D-150 | 0.01 | ||
| 介电常数 | 1MHz | ASTM D-150 | 2.96 | ||
| 体积电阻率 | ASTM D-257 | 1.0×1017 | Ohm-cm | ||
| 热性能 | 阻燃性 | UL94 | 1.1 | mm | |
| 线膨胀系数 | E831 | 6.8×10-5 | 1/°C | ||
| 热变形强度 | 0.45MPa | ASTM D-648 | 137 | °C | |
| UL长期使用温度 | UL746B | 130 | °C | ||
| 维卡软化点 | ASTM D-1525 | 154 | °C | ||
| 阻燃性 | UL94 | HB | |||
| 热变形温度 | 1.8MPa | ASTM D-648 | 132 | °C | |