| 产地/厂家：日本高达 | 类型：标准料 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 比重 | ASTM D792 | 1.20 | |||
| 机械性能 | Izod冲击强度 | - | ASTM D256 | 740 | J/m | |
| - | ASTM D256 | 75 | Kgf.cm/cm | |||
| - | ASTM D256 | 14 | ft.ibf/in | |||
| 拉伸强度 | - | ASTM D638 | 63 | MPa | ||
| - | ASTM D638 | 640 | Kgf/cm2 | |||
| - | ASTM D638 | 9100 | Ibf/in2 | |||
| 断裂伸长率 | ASTM D638 | 120 | % | |||
| 弯曲强度 | - | ASTM D790 | 85 | MPa | ||
| - | ASTM D790 | 870 | Kgf/cm2 | |||
| - | ASTM D790 | 12400 | Ibf/in2 | |||
| 弯曲模量 | - | ASTM D790 | 2160 | MPa | ||
| - | ASTM D790 | 22000 | Kgf/cm2 | |||
| - | ASTM D790 | 313000 | Ibf/in2 | |||
| 电气性能 | 体积电阻率 | ASTM D257 | 1016 | Ω.cm | ||
| 热性能 | 熔体指数 | 300℃,1.2kg | ASTM D1238 | 20 | g/10min | |
| 热变形温度 | 18.6kg/cm2 | ASTM D648 | 133 | ℃ | ||
| 热变形温度 | 18.6kg/cm2 | ASTM D648 | 271 | ℉ | ||